ISO 1456:2003
Metallic coatings — Electrodeposited coatings of nickel plus chromium and of copper plus nickel plus chromium
ISO 1456 specifies the requirements for decorative, electroplated nickel plus chromium, and copper plus nickel plus chromium coatings on iron, steel, zinc alloys, copper and copper alloys, and aluminium and aluminium alloys to provide an attractive appearance and enhanced corrosion resistance. Coating designations are specified that differ in thickness and type, and guidance is given in selecting the coating designation appropriate to the service conditions to which the coated product will be exposed.
| Get this standard | Prices exclude GST | |
|---|---|---|
| PDF ( Single user document) |
$118.26 NZD
|
|
| HardCopy |
$152.17 NZD
|
|
| Networkable PDF |
Price varies
|
TitlePage - Metallic coatings— Electrodeposited coatings of nickel plus chromium and of copper p...
TableofContent - Contents Page
Foreword - Foreword
Introduction - Introduction
Scope - 1 Scope
NormativeReference - 2 Normative references
Clause1 - 4 Information to be supplied by the purchaser to the electroplater
Subclause2 - 4.1 Essential information
Subclause2 - 4.2 Additional information
Clause1 - 5 Service condition number
Clause1 - 6 Designation
Subclause2 - 6.1 General
Subclause2 - 6.2 Type of copper coating
Subclause2 - 6.3 Types of nickel coating
Subclause2 - 6.4 Types and thicknesses of chromium
Subclause2 - 6.5 Designation
Clause1 - 7 Requirements
Subclause2 - 7.1 Appearance
Subclause2 - 7.2 Local thickness
Subclause2 - 7.3 Double- and triple-layer nickel coatings
Subclause2 - 7.4 Adhesion
Subclause2 - 7.5 Corrosion resistance in CASS, Corrodkote and acetic acid salt spray tests
Subclause2 - 7.6 STEP test requirements
Subclause2 - 7.7 Ductility
Subclause2 - 7.8 Stress relief treatments before coating
Subclause2 - 7.9 Hydrogen embrittlement relief treatment
Clause1 - 8 Sampling
AnnexInformative - Examples of service conditions for which the various service condition numbers...
Clause1 - A.1 Service condition number5
Clause1 - A.2 Service condition number4
Clause1 - A.3 Service condition number3
Clause1 - A.4 Service condition number2
Clause1 - A.5 Service condition number1
AnnexNormative - Determination of cracks and pores in chromium coatings
Clause1 - B.1 General
Clause1 - B.2 Microscopical examination for cracks without pre-treatment
Clause1 - B.3 Copper deposition method for cracks and pores
Subclause2 - B.3.1 Principle
Subclause2 - B.3.2 Procedure
AnnexNormative - Methods of test for the determination of thickness
Clause1 - C.1 General
Clause1 - C.2 Destructive
Subclause2 - C.2.1 Microscopical method
Subclause2 - C.2.2 Coulometric method
Subclause2 - C.2.3 Scanning electron microscope method
Subclause2 - C.2.4 STEP Test
Clause1 - C.3 Non-destructive
Subclause2 - C.3.1 Magnetic method (applicable to nickel coatings only)
Subclause2 - C.3.2 Beta backscatter method (applicable only in the absence of copper undercoats)
Subclause2 - C.3.3 X-Ray spectrometry
AnnexNormative - Ductility test
Clause1 - D.1 Scope
Clause1 - D.2 Principle
Clause1 - D.3 Apparatus
UntitledSubclause2 - D.3.1 Mandrel
Clause1 - D.4 Preparation of test piece
Clause1 - D.5 Procedure
Clause1 - D.6 Expression of results
AnnexNormative - Determination of the sulfur content of electrodeposited nickel
Clause1 - E.1 Determination by combustion and iodate titrimetry
Clause1 - E.2 Determination by sulfide formation and iodate titrimetry
Bibliography - Bibliography
Previous versions
Keep me up-to-date
Register to receive notifications when updates are made to this standard.
Related Information
Similar Standards
-
AS/NZS 1214:2016
Hot-dip galvanized coatings on threaded fasteners (ISO metric coarse thread series) -
AS/NZS 1789:2023
Metallic and other inorganic coatings — Electroplated coatings of zinc with supplementary treatments on iron or steel (ISO 2081:2018, MOD)
-
AS/NZS 4534:2006
Zinc and zinc/aluminium-alloy coatings on steel wire
-
AS/NZS 4680:2006
Hot-dip galvanized (zinc) coatings on fabricated ferrous articles
TitlePage - Metallic coatings— Electrodeposited coatings of nickel plus chromium and of copper p...
TableofContent - Contents Page
Foreword - Foreword
Introduction - Introduction
Scope - 1 Scope
NormativeReference - 2 Normative references
Clause1 - 4 Information to be supplied by the purchaser to the electroplater
Subclause2 - 4.1 Essential information
Subclause2 - 4.2 Additional information
Clause1 - 5 Service condition number
Clause1 - 6 Designation
Subclause2 - 6.1 General
Subclause2 - 6.2 Type of copper coating
Subclause2 - 6.3 Types of nickel coating
Subclause2 - 6.4 Types and thicknesses of chromium
Subclause2 - 6.5 Designation
Clause1 - 7 Requirements
Subclause2 - 7.1 Appearance
Subclause2 - 7.2 Local thickness
Subclause2 - 7.3 Double- and triple-layer nickel coatings
Subclause2 - 7.4 Adhesion
Subclause2 - 7.5 Corrosion resistance in CASS, Corrodkote and acetic acid salt spray tests
Subclause2 - 7.6 STEP test requirements
Subclause2 - 7.7 Ductility
Subclause2 - 7.8 Stress relief treatments before coating
Subclause2 - 7.9 Hydrogen embrittlement relief treatment
Clause1 - 8 Sampling
AnnexInformative - Examples of service conditions for which the various service condition numbers...
Clause1 - A.1 Service condition number5
Clause1 - A.2 Service condition number4
Clause1 - A.3 Service condition number3
Clause1 - A.4 Service condition number2
Clause1 - A.5 Service condition number1
AnnexNormative - Determination of cracks and pores in chromium coatings
Clause1 - B.1 General
Clause1 - B.2 Microscopical examination for cracks without pre-treatment
Clause1 - B.3 Copper deposition method for cracks and pores
Subclause2 - B.3.1 Principle
Subclause2 - B.3.2 Procedure
AnnexNormative - Methods of test for the determination of thickness
Clause1 - C.1 General
Clause1 - C.2 Destructive
Subclause2 - C.2.1 Microscopical method
Subclause2 - C.2.2 Coulometric method
Subclause2 - C.2.3 Scanning electron microscope method
Subclause2 - C.2.4 STEP Test
Clause1 - C.3 Non-destructive
Subclause2 - C.3.1 Magnetic method (applicable to nickel coatings only)
Subclause2 - C.3.2 Beta backscatter method (applicable only in the absence of copper undercoats)
Subclause2 - C.3.3 X-Ray spectrometry
AnnexNormative - Ductility test
Clause1 - D.1 Scope
Clause1 - D.2 Principle
Clause1 - D.3 Apparatus
UntitledSubclause2 - D.3.1 Mandrel
Clause1 - D.4 Preparation of test piece
Clause1 - D.5 Procedure
Clause1 - D.6 Expression of results
AnnexNormative - Determination of the sulfur content of electrodeposited nickel
Clause1 - E.1 Determination by combustion and iodate titrimetry
Clause1 - E.2 Determination by sulfide formation and iodate titrimetry
Bibliography - Bibliography