AS/NZS 3750.2:2008
Paints for steel structures - Ultra high-build paint
Specifies requirements for two-component ultra high-build paints for the protection of iron and steel against exterior corrosion in aggressive service conditions.
PREFACE
CONTENTS
SECTION 1 SCOPE AND GENERAL
1.1 SCOPE
1.2 REFERENCED DOCUMENTS
1.3 DEFINITIONS
1.3.1 Gel time
1.3.2 Ultra high-build paint (UHB paint)
1.4 SAFETY PRECAUTIONS
1.4.1 Type I paint
1.4.2 Type II and III paints
SECTION 2 MATERIALS REQUIREMENTS
2.1 GENERAL
2.2 CONDITIONS OF TEST
2.3 LIQUID PAINT
2.3.1 Condition in container
2.3.2 Mass solids
2.3.3 Storage properties
2.4 SPRAY APPLICATION PROPERTIES
2.4.1 General
2.4.2 Sprayability and sag resistance
2.4.3 Pot-life
2.5 APPLIED FILM
2.5.1 General
2.5.2 Hardness
2.5.3 Impact resistance
2.5.4 Abrasion resistance
2.5.5 Adhesion
2.5.6 Cathodic disbondment resistance
2.6 MIXING RATIO
2.7 ADDITIONAL TESTS
SECTION 3 PACKAGING AND LABELLING
3.1 PACKAGING
3.2 LABELLING
APPENDIX A - PURCHASING GUIDELINES
A1 GENERAL
A2 INFORMATION TO BE SUPPLIED WITH THE ENQUIRY OR ORDER
APPENDIX B - GUIDANCE ON THE USE AND APPLICATION OF UHB PAINT
B1 SCOPE
B2 MANUFACTURER’S TECHNICAL DATA
B3 SAFETY PRECAUTIONS
B3.1 Type I paint
B3.2 Type II and Type III paint
B4 APPLICATION AND TYPICAL USES
APPENDIX C - REFERENCED DOCUMENTS
APPENDIX D - PREPARATION OF TEST PANELS
D1 SCOPE
D2 TEST PANEL MATERIAL
D3 PREPARATION
APPENDIX E - DETERMINATION OF THE GEL TIME OF POLYESTER AND VINYL ESTER UHB PAINT
E1 SCOPE
E2 PRINCIPLE
E3 REAGENT
E4 APPARATUS
E4.1 Gel time meter
E4.2 Constant temperature bath
E4.3 Waxed paper cups
E4.4 Pipette
E4.5 Top pan balance
E4.6 Timing device
E4.7 Thermometer
E5 PROCEDURE
APPENDIX F - ADDITIONAL TESTS
F1 SCOPE
F2 GENERAL
F3 TENSILE STRENGTH AT BREAK
F4 COMPRESSIVE STRENGTH
F5 PERCENT ELONGATION AT BREAK
F6 FLEXURAL STRENGTH AT BREAK
F7 MODULUS OF ELASTICITY
Keep me up-to-date
Sign up to receive updates when there are changes to this standard
Related Information
Similar Standards
-
AS/NZS 1554.1:2014
Structural steel welding - Part 1: Welding of steel structures -
AS/NZS 1554.1:2014 A1
Structural steel welding - Part 1: Welding of steel structures: Amendment 1 -
AS/NZS 1554.1:2014 A2
Structural steel welding - Part 1: Welding of steel structures: Amendment 2 -
AS/NZS 1554.2:2003
Structural steel welding - Stud welding (steel studs to steel)
PREFACE
CONTENTS
SECTION 1 SCOPE AND GENERAL
1.1 SCOPE
1.2 REFERENCED DOCUMENTS
1.3 DEFINITIONS
1.3.1 Gel time
1.3.2 Ultra high-build paint (UHB paint)
1.4 SAFETY PRECAUTIONS
1.4.1 Type I paint
1.4.2 Type II and III paints
SECTION 2 MATERIALS REQUIREMENTS
2.1 GENERAL
2.2 CONDITIONS OF TEST
2.3 LIQUID PAINT
2.3.1 Condition in container
2.3.2 Mass solids
2.3.3 Storage properties
2.4 SPRAY APPLICATION PROPERTIES
2.4.1 General
2.4.2 Sprayability and sag resistance
2.4.3 Pot-life
2.5 APPLIED FILM
2.5.1 General
2.5.2 Hardness
2.5.3 Impact resistance
2.5.4 Abrasion resistance
2.5.5 Adhesion
2.5.6 Cathodic disbondment resistance
2.6 MIXING RATIO
2.7 ADDITIONAL TESTS
SECTION 3 PACKAGING AND LABELLING
3.1 PACKAGING
3.2 LABELLING
APPENDIX A - PURCHASING GUIDELINES
A1 GENERAL
A2 INFORMATION TO BE SUPPLIED WITH THE ENQUIRY OR ORDER
APPENDIX B - GUIDANCE ON THE USE AND APPLICATION OF UHB PAINT
B1 SCOPE
B2 MANUFACTURER’S TECHNICAL DATA
B3 SAFETY PRECAUTIONS
B3.1 Type I paint
B3.2 Type II and Type III paint
B4 APPLICATION AND TYPICAL USES
APPENDIX C - REFERENCED DOCUMENTS
APPENDIX D - PREPARATION OF TEST PANELS
D1 SCOPE
D2 TEST PANEL MATERIAL
D3 PREPARATION
APPENDIX E - DETERMINATION OF THE GEL TIME OF POLYESTER AND VINYL ESTER UHB PAINT
E1 SCOPE
E2 PRINCIPLE
E3 REAGENT
E4 APPARATUS
E4.1 Gel time meter
E4.2 Constant temperature bath
E4.3 Waxed paper cups
E4.4 Pipette
E4.5 Top pan balance
E4.6 Timing device
E4.7 Thermometer
E5 PROCEDURE
APPENDIX F - ADDITIONAL TESTS
F1 SCOPE
F2 GENERAL
F3 TENSILE STRENGTH AT BREAK
F4 COMPRESSIVE STRENGTH
F5 PERCENT ELONGATION AT BREAK
F6 FLEXURAL STRENGTH AT BREAK
F7 MODULUS OF ELASTICITY